Studying the Deformation Resistance of Ep679 Maraging Steel

S. V. Gladkovsky; A. I. Potapov; S. V. Lepikhin

doi:10.17804/2410-9908.2015.4.018-028

S. V. Gladkovsky, A. I. Potapov, S. V. Lepikhin

STUDYING THE DEFORMATION RESISTANCE OF EP679 MARAGING STEEL

DOI: 10.17804/2410-9908.2015.4.018-028

The resistance of high-strength maraging steel EP679 to plastic deformation σs is studied as dependent on the amount of strain, strain rate and deformation temperature, as well as on heat-treatment conditions. Quantitative evaluation is obtained and regularities are found in the change of σs values depending on the studied factors, with the structural evolution of steel under heating and cooling taken into account. A positive effect of preheating up to 920 °C and subsequent cooling to the test temperature on the decrease in the value of σs during subsequent deformation at temperatures ranging between 20 and 900 °C is shown.

Acknowledgements: 1. Perkas M.D., Kardonsky V.M. Vysokoprochnye martensitno-stareyushchie stali [High-strength maraging steels]. Moscow, Metallurgiya Publ., 1970, 224 p. (In Russian). 2. Georgiev M.N., Simonov Yu.N. Treshchinostoykost zhelezouglerodistykh splavov [Crack resistance of iron-carbon alloys]. Perm, Izdatelstvo Permskogo natsionalnogo issledovatelskogo politekhnicheskogo universiteta Publ., 2013, 419 p. (In Russian). 3. Efros B.M., Konakova I.P., Gladkovsky S.V., Tyutenko V.S., Loladze L.V., Zaika T.P., Varyukhin V.N. Effect of the conditions of thermoplastic treatment on the deformation resistance, mechanical properties and crack resistance of cobalt-free maraging steels. Fizika i tekhnika vysokikh davleny, 1997, vol. 7, no. 4, pp. 5–23. (In Russian). 4. Veksler Yu.G., Zvigintsev N.V., Konakova I.P., Belova G.V., Suntsev G.N. Deformability of steel 03Kh11N10M2T at temperatures ranging between 20 and 1100°С. Izvestiya vuzov. Chernaya metalluriya, 1986, no. 8, pp. 74–78. (In Russian). 5. Potapov A.I., Mazunin V.P., Dvoynikov D.A., Kokovikhin E.A. Methods for studying deformation resistance on a plastometric complex. Zavodskaya laboratoriya. Diagnostika materialov, 2010, vol. 76, no. 9, pp. 59–63. (In Russian). 6. Terentiev V.V., Bunin I.Zh., Zagreev P.V. Effect of the aging temperature on the complex of mechanical properties of maraging steel. Materialovedenie, 1998, no. 1, pp. 40–49. (In Russian). 7. Tarasenko L.V., Zvigintsev N.V., Titov V.I., Khadyev M.S. Phase transformations in steel 00Kh11M2T…T1 under long-term aging. FMM, 1987, vol. 63, iss. 4, no. 6, pp. 768–773. (In Russian). 8. Shaposhnikov N.G., Mogutnov B.M., Zvigintsev N.V., Khadyev M.S. Termodinamicheskiy analiz fazovykh ravnovesiy v martensitnostareyushchikh stalyakh. In: Heat treatment, structure and properties of metals. Interuniv. coll., Sverdlovsk, UPI Publ., 1985, iss. 10, pp. 3–9. (In Russian). 9. Georgiev M.N., Simonov Yu.N. Treshchinostoykost zhelezouglerodistykh splavov [Crack resistance of iron-carbon alloys]. Perm, PNRPU Publ., 2013, 419 p. (In Russian). 10. Vylezhnev V.P., Sukhikh A.A., Bragin V.G., Kokovyakina S.A. Mechanical properties of grade N18K9M5T maraging steel containing retained and reversed austenite. The Physics of Metals and Metallography, 1993, vol. 75, no. 4, pp. 157–165. 11. Gladkovsky S.V., Zvigintsev N.V., Kruglov A.A., Doroshkevich T.A., Fazliakhmetov R.S., Yurovskikh V.V. Effect of structural transformations on the mechanical properties and crack resistance of cobalt-free maraging steels. FMM, 1990, iss. 2, pp. 106–113. (In Russian).

Keywords: maraging steel, deformation resistance, plastometric tests, structure, phase transformations

Bibliography:

1. Perkas M.D., Kardonskiy V.M. Vyisokoprochnyie martensitno-stareyuschie stali. - M.: Metallurgiya, 1970. - 224 s.

2. Georgiev M.N., Simonov Yu.N. Treschinostoykost zhelezouglerodistyikh splavov. – Perm: Izd-vo Perm. nac. issled. politekh. un-ta, 2013. – 419 s.

3. Vliyanie usloviy termoplasticheskoy obrabotki na soprotivlenie deformacii, mekhanicheskie svoystva i treschinostoykost beskobaltovyikh martensitno-stareyuschikh staley / B.M. Yefros, I.P. Konakova, S.V. Gladkovskiy, V.S. Tyutenko, L.V. Loladze, T.P. Zaika, V.N. Varyukhin // Fizika i tekhnika vyisokikh davleniy. – 1997. - Tom. 7. - № 4. - S. 5-23.

4. Deformiruemost stali 03Kh11N10M2T v intervale temperatur 20 – 1100 oS / Yu.G. Veksler, N.V. Zvigincev, I.P. Konakova, G.V. Belova, G.N. Suncev // Izvestiya vuzov. Chernaya metallurgiya. – 1986. - № 8. - S. 74– 78.

5. Metodika issledovaniya soprotivleniya deformacii na plastometricheskom komplekse / A.I. Potapov, V.P. Mazunin, D.A. Dvoynikov, E.A. Kokovikhin // Zavodskaya laboratoriya. Diagnostika materialov. – 2010. - № 9. - T.76. - S.59–63.

6. Terentev V.V., Bunin I.Zh., Zagreev P.V. Vliyanie temperaturyi stareniya na kompleks mekhanicheskikh svoystv martensitnostareyuschey stali // Materialovedenie – 1998. - № 1. - S. 40-49.

7. Tarasenko L.V., Zvigincev N.V., Titov V.I., Khadyiev M.S. Fazovyie prevrascheniya pri dlitelnom starenii stali 00Kh11M2T…T1 // FMM. - 1987, - T. 63. - Vyip 4. - № 6. - S. 768-773.

8. Termodinamicheskiy analiz fazovyikh ravnovesiy v martensitnostareyuschikh stalyakh / N.G. Shaposhnikov, B.M. Mogutnov, N.V. Zvigincev, M.S. Khadyiev // Termicheskaya obrabotka, struktura i svoystva metallov. Vyip.10. Mezhvuz. sb. Sverdlovsk: Izd-vo UPI im. S.M. Kirova, 1985. - S. 3-9.

9. Georgiev M.N., Simonov Yu.N. Treschinostoykost zhelezouglerodistyikh splavov. – Perm: Izd-vo Perm. Nac. Issled. Politekhn.un-ta, 2013. – 419 s.

10. Mekhanicheskie svoystva martensitnostareyuschey stali N18K8M5T s ostatochnyim i revertirovannyim austenitom / V.P. Vyilezhnev, A.A. Sukhikh, V.G. Bragin, S.A. Kokovyakina // FMM. - 1993. - T.75. - Vyip. 4. - S. 157-165.

11. Vliyanie strukturnyikh prevrascheniy na mekhanicheskie svoystva i treschinostoykost beskobaltovyikh martensitno-stareyuschikh staley / S.V. Gladkovskiy, N.V. Zvigincev, A.A. Kruglov, T. A. Doroshkevich, R. S. Fazliakhmetov, V. V. Yurovskikh // FMM. - 1990. - Vyip. 2. - S. 106-113.

С. В. Гладковский, А. И. Потапов, С. В. Лепихин

ИССЛЕДОВАНИЕ СОПРОТИВЛЕНИЯ ДЕФОРМАЦИИ МАРТЕНСИТНО-СТАРЕЮЩЕЙ СТАЛИ ЭП679

Проведено исследование сопротивления пластической деформации σs высокопрочной мартенситно-стареющей стали ЭП679 в зависимости от степени, скорости, температуры деформации и режима термической обработки. Получена количественная оценка и установлены закономерности изменения величины σs в зависимости от исследуемых факторов, с учетом структурных изменений в стали при нагреве и охлаждении. Показано положительное влияние предварительного нагрева до 920 °С и последующего охлаждения до температуры испытания на снижение величины σs при последующей деформации в интервале температур от 20 до 900 °С.

Ключевые слова: мартенсито-стареющая сталь, сопротивление деформации, пластометрические испытания, структура, фазовые превращения

Библиография:

Перкас М. Д., Кардонский В. М. Высокопрочные мартенситно-стареющие стали. – М. : Металлургия, 1970. – 224 с.
Георгиев М. Н., Симонов Ю. Н. Трещиностойкость железоуглеродистых сплавов. – Пермь : Изд-во Перм. нац. исслед. политехн. ун-та, 2013. – 419 с.
Влияние условий термопластической обработки на сопротивление деформации, механические свойства и трещиностойкость бескобальтовых мартенситно-стареющих сталей / Б. М. Эфрос, И. П. Конакова, С. В. Гладковский, В. С. Тютенко, Л. В. Лоладзе, Т. П. Заика, В. Н. Варюхин // Физика и техника высоких давлений. – 1997. – Том. 7, № 4. – С. 5–23.
Деформируемость стали 03Х11Н10М2Т в интервале температур 20–1100^оС / Ю. Г. Векслер, Н. В. Звигинцев, И. П. Конакова, Г. В. Белова, Г. Н. Сунцев // Известия вузов. Черная металлургия. – 1986. – № 8. – С. 74– 78.
Методика исследования сопротивления деформации на пластометрическом комплексе / А. И. Потапов, В. П. Мазунин, Д. А. Двойников, Е. А. Коковихин // Заводская лаборатория. Диагностика материалов. – 2010. – Т. 76, № 9. – С. 59–63.
Терентьев В. В., Бунин И. Ж., Загреев П. В. Влияние температуры старения на комплекс механических свойств мартенситностареющей стали // Материаловедение – 1998. – № 1. – С. 40–49.
Тарасенко Л. В., Звигинцев Н. В., Титов В. И., Хадыев М. С. Фазовые превращения при длительном старении стали 00Х11М2Т…Т1 // ФММ. – 1987. – Т. 63, вып 4, № 6. – С. 768–773.
Термодинамический анализ фазовых равновесий в мартенситностареющих сталях / Н. Г. Шапошников, Б. М. Могутнов, Н. В. Звигинцев, М. С. Хадыев // Термическая обработка, структура и свойства металлов межвуз. сб. – Свердловск : Изд-во УПИ им. С. М. Кирова, 1985. – Вып.10. – С. 3–9.
Георгиев М. Н., Симонов Ю. Н. Трещиностойкость железоуглеродистых сплавов. – Пермь : Изд-во Перм. Нац. Исслед. Политехн. ун-та, 2013. – 419 с.
Механические свойства мартенситностареющей стали Н18К8М5Т с остаточным и ревертированным аустенитом / В. П. Вылежнев, А. А. Сухих, В. Г. Брагин, С. А. Коковякина // ФММ. – 1993. – Т. 75, вып. 4. – С. 157–165.
Влияние структурных превращений на механические свойства и трещиностойкость бескобальтовых мартенситно-стареющих сталей / С. В. Гладковский, Н. В. Звигинцев, А. А. Круглов, Т. А. Дорошкевич, Р. С. Фазлиахметов, В. В. Юровских // ФММ. – 1990. – Вып. 2. – С. 106–113.

Библиографическая ссылка на статью

Gladkovsky S. V., Potapov A. I., Lepikhin S. V. Studying the Deformation Resistance of Ep679 Maraging Steel // Diagnostics, Resource and Mechanics of materials and structures. - 2015. - Iss. 4. - P. 18-28. -
DOI: 10.17804/2410-9908.2015.4.018-028. -
URL: http://dream-journal.org/issues/2015-4/2015-4_32.html
(accessed: 25.04.2024).